Powder and single-crystal x-ray study of chromium chlorine boracite, Cr3B7O13Cl, at low temperature. Powder refinement of the orthorhombic modification at 100 K

ContributorsMao, Shao Yu; Kubel, Frank; Schmid, Hans; Yvon, Klaus
Published inFerroelectrics, vol. 132, no. 1-4, p. 239-244
Publication date1992
Abstract

Cr3B7O13Cl: space group Pca21, a 8.5647(2), b 8.6125(2), c 12.1453(3) .ANG., Rp = 0.0273, RB = 0.0723 was refined from x-ray powder profile data at T = 100 K. Lattice parameters as measured on single-crystals and powders show a discontinuous vol. increase of 0.45% at the cubic-to-tetragonal phase transition at 264 K, but practically no vol. change (<001%) at the tetragonal-to-orthorhombic phase transition at 180 K. The metal coordinations in the orthorhombic low-temp. modification differ less from those in the cubic high-temp. modification than in other boracites.

Keywords
  • Crystal structure
  • Chromium chlorine boracite
Affiliation entities
Funding
  • Swiss National Science Foundation - 1991
Citation (ISO format)
MAO, Shao Yu et al. Powder and single-crystal x-ray study of chromium chlorine boracite, Cr3B7O13Cl, at low temperature. Powder refinement of the orthorhombic modification at 100 K. In: Ferroelectrics, 1992, vol. 132, n° 1-4, p. 239–244.
Main files (1)
Article (Published version)
accessLevelPublic
Identifiers
  • PID : unige:31412
Journal ISSN0015-0193
664views
621downloads

Technical informations

Creation10/11/2013 14:21:00
First validation10/11/2013 14:21:00
Update14/03/2023 20:38:39
Status update14/03/2023 20:38:39
Last indexation30/10/2024 15:04:36
All rights reserved by Archive ouverte UNIGE and the University of GenevaunigeBlack