Objectives: To study the potential benefits of a post-cure thermal treatment on key physico-mechanical properties of light-cured resin-based composites for use in indirect restorations, a CAD/CAM composite block being used as control.

Material and methods: Six commercial composites were light-cured before being thermally treated in a furnace at 90°C during 15 minutes (CAD/CAM composite used as a control). The properties measured with or without thermal treatment were: degree of conversion, flexural strength, elastic modulus, Vickers microHardness, organic mass content and eluted and absorbed mass before and after storage in ethanol. The data were analysed using one-way ANOVA, and Weibull distributions.

Results: A general increase in the properties measured was observed for all materials after thermal treatment, except a general decrease in mass elution and absorption (most statistically significant: p⟨0.05). Weibull analysis showed a tendency (p⟩0.05) of increased reliability of the flexural strength after thermal treatment for all materials.

Conclusion: The present data revealed clear physico-mechanical improvements after thermal treatment of light-cured composites. Such method could hence be beneficially used to produce indirect restorations as compared to stratifying and light-curing the same composites in situ. However, most properties of the control CAD/CAM composite were higher, but CAD/CAM technologies aren't available everywhere.