Microstructure, resistivity and critical currents of Ag-Bi/Pb(2223) tapes

Perin, A.
Pollini, A.
Published in IEEE Transactions on Applied Superconductivity. 1993, vol. 3, no. 1, p. 1139-1142
Abstract The temperature and field dependences of critical current density, j/sub c/, in Ag-Bi/Pb(2223) tapes, prepared by the standard powder-in-tube method, have been measured between 4.2 K and 110 K in magnetic fields up to 15 T. The j/sub c/'s reproducibly reached values up to 20000 A/cm/sup 2/ at 77.35 K in zero magnetic field. After stripping or etching away the Ag-sheath, the microstructure of the superconductor core has been investigated by SEM, EDX and X-ray diffraction. On etched samples the resistance of the Bi(2223) filament has been measured. A value below 500 mu Omega -cm has been found for the resistivity at 130 K.
Full text
Article (Published version) (2.7 MB) - document accessible for UNIGE members only Limited access to UNIGE
Other version: http://ieeexplore.ieee.org/document/233353/
(ISO format)
HENSEL, Bernhard et al. Microstructure, resistivity and critical currents of Ag-Bi/Pb(2223) tapes. In: IEEE Transactions on Applied Superconductivity, 1993, vol. 3, n° 1, p. 1139-1142. doi: 10.1109/77.233353 https://archive-ouverte.unige.ch/unige:105007

199 hits

0 download


Deposited on : 2018-06-05

Export document
Format :
Citation style :